| Zug- und Härteanforderungen |
| Note |
|
|
Streckgrenze MPa |
Zug Stärke |
Härte a,c |
Angegebene Wandstärke |
Zulässige Härte Variante b |
| |
Typ |
Gesamtdehnung unter Last |
|
min MPa |
max |
|
|
| |
|
|
min |
max |
|
HRC |
HBW |
mm |
HRC |
| 1 |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
| H40 |
|
0.5 |
276 |
552 |
414 |
|
|
|
|
| J55 |
|
0.5 |
379 |
552 |
517 |
|
|
|
|
| K55 |
|
0.5 |
379 |
552 |
655 |
|
|
|
|
| N80 |
1 |
0.5 |
552 |
758 |
689 |
|
|
|
|
| N80 |
Q |
0.5 |
552 |
758 |
689 |
|
|
|
|
| R95 |
|
0.5 |
655 |
758 |
724 |
|
|
|
|
| L80 L80 |
1 |
0.5 |
552 |
655 |
655 |
23 |
241 |
|
|
| L80 |
9Cr 13Cr |
0.5 |
552 |
655 |
655 |
23 |
241 |
|
|
| |
|
0.5 |
552 |
655 |
655 |
23 |
241 |
|
|
| C90 |
1 |
0.5 |
621 |
724 |
689 |
25.4 |
255 |
12,70 |
3 |
| |
|
|
|
|
|
|
|
12.71 bis 19.04 |
4 |
| |
|
|
|
|
|
|
|
19.05 bis 25.39 |
5 |
| |
|
|
|
|
|
|
|
25,40 |
6 |
| T95 |
1 |
0.5 |
655 |
758 |
724 |
25.4 |
255 |
12,70 |
3 |
| |
|
|
|
|
|
|
|
12.71 bis 19.04 |
4 |
| |
|
|
|
|
|
|
|
19.05 bis 25.39 |
5 |
| |
|
|
|
|
|
|
|
25,40 |
6 |
| C110 |
|
0.7 |
758 |
828 |
793 |
30 |
286 |
12,70 |
3 |
| |
|
|
|
|
|
|
|
12.71 bis 19.04 |
4 |
| |
|
|
|
|
|
|
|
19.05 bis 25.39 |
5 |
| |
|
|
|
|
|
|
|
25,40 |
6 |
| P110 |
|
0.6 |
758 |
965 |
862 |
|
|
|
|
| Q125 |
1 |
0.65 |
862 |
1034 |
931 |
b |
|
12,70 |
3 |
| |
|
|
|
|
|
|
|
12.71 bis 19.04 19.05 |
4 |
| |
|
|
|
|
|
|
|
|
5 |
| a Im Streitfall wird die Rockwell-C-Härteprüfung im Labor als Referenzmethode verwendet. |
| b Es sind keine Härtegrenzen festgelegt, die maximale Abweichung ist jedoch als Fertigungskontrolle gemäß 7.8 und 7.9 eingeschränkt. |
| c Für Härteprüfungen durch die Wand der Klassen L80 (alle Typen), C90, T95 und C110 gelten die in der HRC-Skala angegebenen Anforderungen für die maximale mittlere Härtezahl. |